Corrosion Resistant and Graphite Oxide Resistant Tank

• Type: Graphite Mold
• Composition: 99.9% High Purity Graphite
• Carbon Content: High-Carbon
• Grade: High Purity Graphite
• Forming Way: Molded Graphite
• Crystal Morphology: Compact Crystalline Graphite
• Model NO.: LT-M
• Density: 1.70-1.92g/cm3
• Resistivity: Less Than 12
• Compressive Strength: More Than 70MPa
• Porosity: Less Than 26%
• Elasticity Modulus: 6-18gpa
• Thermal Expansion Coefficient: 1.47-4.25
• Temperature Resistance: Less Than 4350 Degree
• Ash Content: Less Than 0.05%
• Surface Process: Machining
• Transport Package: Cartons in Wooden Cases
• Specification: personalized customized
• Trademark: L. T
• Origin: Cn
• HS Code: 3801909000
• Production Capacity: 300000 Pieces/Month

Product Description

     

               Corrosion resistant and graphite oxide resistant tank

                                                                          lttrade.en.made-in-china.com





A: Company profile
   

   L.T Group has a comprehensive product and technology portfolio that focuses on four fields ofgraphite - ultrafine particle
graphite mould, graphite electrode, graphite crucible, as well as other products mainly made of graphite.




B: Why choose us
 
 Graphite product plays a dual role in the process of diamond tools manufacture:Heating element and Supporting mold.The quality of graphite mold is very important, will directly affect the next diamond tools' accuracy and appearance.So, which kind of graphite mold is suitable for sintering diamond tools:
 
  a: Good performance on conductivity and high rate resistivity
  b: Enough Mechanical Strength
  c: Good performance on Oxidation resistance
  d: Durable
  



c: Tech Data

Granularity  mm	0.8	0.8	2	2
	LTGM-1	LTGM-2	LTGM-1	LTGM-2
Density  g/cm³	≥1.58	≥1.70	≥1.58	≥1.70
Resistivity  μΩ·m	≤12	≤8.5	≤12	≤9
Compressive strength  Mpa	≥19	≥35	≥19	≥30
Bending strength	≥7.8	≥13.5	≥7.8	≥13
Thermal expansion coefficient  10-6/ºC	≤2.0	≤2.2	≤2.0	≤2.2
Ash content  %	≤0.3	≤0.3	≤0.3	≤0.3

 

Description	LT-4	LT-5	LT-7	LT-8
Density  g/cm³	1.8	1.85	1.85	1.91
Electrical Resistivity  uΩ·m	10-12	8.5-10	11-13	11-13
Flexural Strength  MPa	43	46	51	60
Compressive Strength  MPa	80	85	115	135
Thermal Conductivity  W/m*K	110	139.2	85	85
Temperature resistance ºC	4350	4350	4350	4350
Ash content  %	0.03	0.03	0.03	0.03